Intumescent fireproof coatintgs based on zeolite-like cement matrices

dc.contributor.authorKrivenko Pavel
dc.contributor.authorGuzii Sergii
dc.contributor.authorRudenko Igor
dc.contributor.authorKonstantynovskyi Oleksandr
dc.date.accessioned2024-02-09T14:07:18Z
dc.date.available2024-02-09T14:07:18Z
dc.date.issued2023-09
dc.description.abstractConcrete and reinforced concrete building structures (for example, such as tunnels) lose carrying ability in case of high‐temperature fire action. The aim of the research is to study the prevention of reinforced concrete structures (for example, such as tunnels) under fire action in case of using the proposed coating based on the alkaline aluminosilicate binder, which would not consist of organic components dangerous to health. The ratios between constituent oxides in the binder which ensure the ability to bloat the coating under fire action were determined. The performance properties of developed fire protective coating were defined after artificial aging (cycles of alternate drying and cooling) and fire action: bloating factor ‐ 2.0…5.1, adhesion strength ‐ 6.6…8.0 MPa, compressive strength ‐ 2.3…4.5 MPa, cohesive strength of 1.2…1.5 MPa, thermal conductivity coefficient ‐ 0.042…0.066 W/m‐°C, total porosity ‐ 92…97 %. The temperature at which the coating starts to bloat = 200…250 °C has been developed. The results of the test held in the open air suggested drawing a conclusion that with a coating thickness of 6 mm protection of the reinforced concrete from fragile fracture and from plastic deformations in the metal of the reinforcement they provided under fire exposure for a period of 3 hours.
dc.description.sponsorshipАuthоrs wоuld lіkе tо асknоwlеdgе thе соntrіbutіоn оf thе Rеsеаrсh Соunсіl оf Lіthuаnіа аnd thе Mіnіstry оf Еduсаtіоn аnd Sсіеnсе оf Ukrаіnе prоjесt ‘‘Sоlutіоns tо rеduсе аggrеssіvе іоns SО42- аnd Сl- durіng trаnspоrt іn Pоrtlаnd сеmеnt соnсrеtе wіth stееl rеіnfоrсеmеnt іn hydrаulіс struсturеs”, prоjесt соdе S-LU-22-7.
dc.identifier.citationIntumescent fireproof coatintgs based on zeolite-like cement matrices / P. Krivenko, S. Guzii, I. Rudenko, O. Konstantynovskyi // Proceedings in civil engineering. - 2023. - Vol. 5. - P. 923 - 929. - Bibliogr. : 40 titl.
dc.identifier.doi10.1002/cepa.2214
dc.identifier.issn2509-7075
dc.identifier.issn2509-7075
dc.identifier.urihttps://repositary.knuba.edu.ua/handle/123456789/11991
dc.language.isoen
dc.publisherWiley
dc.relation.ispartofce/papers
dc.relation.ispartofseries6
dc.subjectadhesion
dc.subjectaluminosilicate pellets
dc.subjectcohesion
dc.subjectintumescent coating
dc.subjecttunnel
dc.subjectzeolite-like cement matrices
dc.subjectкафедра технології будівельних конструкцій і виробів
dc.subject.udc666
dc.titleIntumescent fireproof coatintgs based on zeolite-like cement matrices
dc.typejournal-article
oaire.citation.issue5
oaire.citation.volume6
Файли
Контейнер файлів
Зараз показуємо 1 - 1 з 1
Ескіз недоступний
Назва:
2023_INTUMESCENT FIREPROOF COATINGS BASED ON ZEOLITE-LIKE CEMENT MATRICES.pdf
Розмір:
618.64 KB
Формат:
Adobe Portable Document Format
Ліцензійна угода
Зараз показуємо 1 - 1 з 1
Ескіз недоступний
Назва:
license.txt
Розмір:
1.71 KB
Формат:
Item-specific license agreed upon to submission
Опис: